Muhammad Khumaedi, FT P Teknik Mesin and Wirawan Sumbodo, - and Rahmat Doni Widodo, - (2016) The Tensile Strength Properties of CFRPs and GRRPs for Unnes Electric Car Body Material. In: The 3rd International Conference on Advanced Materials Science and Technology (ICAMST 2015).

	PDF - Published Version Download (895kB)
	PDF - Published Version Download (780kB)

Abstract

This paper describes composite materials tensile testing of electric car body material. The UNNES electric car body must be developed using a high strength and lightweight material. A fiber-reinforced plastic composite is widely used for the concerned objective. Selection of the type of composites, variations in fiber orientation, and the number of fiber layers will affect the tensile strength of the material. Composite materials use Carbon-fiber-reinforced plastics (CFRPs) and glass-fiber-reinforced plastics (GFRPs) variation to the fiber areal weight, variations in fiber orientation and the number of fiber layers. The CFRPs areal weight consists of 230 gsm and 400 gsm. The GFRPsareal weight consists of 400 gsm and 600 gsm. Fibre orientationsconsist of 0º and 45º. Number of fiber layers consists of one layer and two layers. Various variations were then tested to figure out their tensile to get ultimate tensile strength of materials. Standard test method for tensile test was conducted using ASTM D3039. Tensile specimen geometry used a type of balanced and symmetric fiber orientation, with 25mm in width, 250 mm in length, and 2.5 mm in thickness. The result shows that the more fiber areal weight and the layer number were used, the more its tensile strength would increase, beside it increased the ultimate tensile strength of the material for both glass and carbon fiber with 0o and 45o fiber arientation. Fiber plain wave with 45o has greater tensile strength compared to any other variation

Actions (login required)

View Item