The particle and crystallite size analysis of BaTiO3 produced by conventional solid-state reaction process.


Mohammad Avicenna Elqudsy, - and Rahmat Doni Widodo, - and Rusiyanto, - and Wirawan Sumbodo, Teknik PTM (2017) The particle and crystallite size analysis of BaTiO3 produced by conventional solid-state reaction process. In: Engineering International Conference (EIC) 2016.

[thumbnail of The particle and crystallite size analysis of BaTiO3 produced by conventional solid-state reaction process.pdf] PDF - Published Version
Download (1MB)
[thumbnail of Turnitin The Particle and Crystallite Size Analysis of BaTiO 3 Produced by Conventional Solid-state Reaction Process (1).pdf] PDF - Published Version
Download (1MB)
[thumbnail of Review The particle and crystallite size analysis of BaTiO3 produced by conventional solid-state reaction process.pdf] PDF - Published Version
Download (220kB)

Abstract

Synthesis of piezoelectric material BaTiO3 was done by conventional solid-state reaction process, is the process that combine betwen mechanical alloying and sintering process with BaCO3 and TiO2 precursors. Different samples were prepared by using vibratory ball milling with ball to powder ratio 10:1 and varying the milling time from 1 h to 60 h. The milled powders were investigated with particle size analyzer (PSA). The sintering process was up to 1200oC and the products were examined by X-Ray Diffractometer (XRD) to analyze phase formation and crystallite size. The results showed that the particle size decreases as the function of milling time and reduced to 0,8 μm at 60 h. Single�phase BaTiO3 were succesfully achieved at 1100oC for 10 h holding time of sintering temperature. The crystallite size of BaTiO3 were sintered at 1200oC for 10 h holding time is 106 nm. Crystallite size of BaTiO3 increase as function of temperature and holding time of sintering process

Item Type: Conference or Workshop Item (Paper)
Subjects: T Technology > TJ Mechanical engineering and machinery
Fakultas: Fakultas Teknik > Pendidikan Teknik Mesin, S1
Depositing User: mahargjo hapsoro adi
Date Deposited: 20 Apr 2022 07:28
Last Modified: 20 Apr 2022 07:28
URI: http://lib.unnes.ac.id/id/eprint/49670

Actions (login required)

View Item View Item