The particle and crystallite size analysis of BaTiO3 produced by conventional solid-state reaction process


Rusiyanto, - (2017) The particle and crystallite size analysis of BaTiO3 produced by conventional solid-state reaction process. AIP Conference Proceedings. ISSN 978-0-7354-1486-0

[thumbnail of 13. The Particle and Crystallite Size Analysis of BaTiO3 Produced by Conventional Solid-state Reaction Process - KUSDIYANTO UNNES.pdf] PDF
Download (1MB)

Abstract

Synthesis of piezoelectric material BaTiO3 was done by conventional solid-state reaction process, is the process that combine betwen mechanical alloying and sintering process with BaCO3 and TiO2 precursors. Different samples were prepared by using vibratory ball milling with ball to powder ratio 10:1 and varying the milling time from 1 h to 60 h. The milled powders were investigated with particle size analyzer (PSA). The sintering process was up to 1200oC and the products were examined by X-Ray Diffractometer (XRD) to analyze phase formation and crystallite size. The results showed that the particle size decreases as the function of milling time and reduced to 0,8 μm at 60 h. Single- phase BaTiO3 were succesfully achieved at 1100oC for 10 h holding time of sintering temperature. The crystallite size of BaTiO3 were sintered at 1200oC for 10 h holding time is 106 nm. Crystallite size of BaTiO3 increase as function of temperature and holding time of sintering process.

Item Type: Article
Subjects: T Technology > TJ Mechanical engineering and machinery
T Technology > TP Chemical technology
Fakultas: Fakultas Teknik > Pendidikan Teknik Mesin, S1
Depositing User: dina nurcahyani perpus
Date Deposited: 13 Jan 2022 03:14
Last Modified: 13 Jan 2022 03:14
URI: http://lib.unnes.ac.id/id/eprint/48362

Actions (login required)

View Item View Item