MANGO (Mangifera indica L.) LEAVES WASTE/POLYVINYL ACETATE BIOCOMPOSITE FOR BUILDING MATERIALS APPLICATION


Masturi, FMIPA Pendidikan Fisika (2020) MANGO (Mangifera indica L.) LEAVES WASTE/POLYVINYL ACETATE BIOCOMPOSITE FOR BUILDING MATERIALS APPLICATION. Malaysian Applied Biology, 49 (2). pp. 49-54. ISSN 0126-8643

[thumbnail of Masturi et al (2020)_MAB - Masturi UNNES.pdf]
Preview
PDF
Download (144kB) | Preview

Abstract

A leaves waste biocomposite was produced via a simple mixing and hot-pressing process. Using mango (Mangifera indica L.) leaves waste as a filler and polyvinyl acetate (PVAc) as a binder, the biocomposite was synthesized at pressure and temperature of 3 metric tons and 40°C, respectively, for 20 minutes. The weight fraction of leaves waste varied obtaining a composite having maximum compressive strength, i.e., 37.82 MPa for leaves waste fraction of 0.62 (w/w). This strength is comparable to several stones such as sandstone stone, limestone, clay brick, aspen wood, and pinewood usually used as building materials. Therefore, the biocomposite is acceptable for building materials application.

Item Type: Article
Uncontrolled Keywords: Mango leaves waste, polyvinyl acetate, biocomposite, compressive strength
Subjects: Q Science > QH Natural history > QH301 Biology
Fakultas: Fakultas Matematika dan Ilmu Pengetahuan Alam > Pendidikan Fisika, S1
Depositing User: dina nurcahyani perpus
Date Deposited: 31 Mar 2021 01:49
Last Modified: 31 Mar 2021 01:49
URI: http://lib.unnes.ac.id/id/eprint/43650

Actions (login required)

View Item View Item